There are various casting processes being implemented now days. The oldest amongst them is sand casting. Spin Casting is also widely used. They can be described as follows:
Sand Casting: Sand Casting involves formation of mold from a mixture of sand and to pour a casting liquid, most probably, a molten metal into mold. To remove the mold, you must wait a little while for the metal to solidify. There are two methods or types of sand molding and those are the green sand method and the air set method. The first one consists of mixture of clay, moisture, silica, and many other additives. The second one consists of mixture of dry sand and other materials, not moist clay. They are mixed with the help of a quick curing adhesive. When all of these materials are used together, it is a process called air set.
At times, there is temporary plug placed to pour the fluid which is to be molded. Air-set molds usually form molds consisting of two parts-the bottom and the top. The mixture of sand gets tamped down after its addition. It does not generate any by-product. After the solidification and cooling of metal, the mold gets usually destroyed. This is because its removal involves a lot of breaking and cracking. The casting accuracy depends a great deal on the sand and the process of molding used. Castings composed of green sand result into formation of rough texture on casting surface, and this characteristic makes them easily recognizable. The smoothest castings are really produced when one uses molds that are air set.
Many a times, the casting process results in losing of components of sand mixture. It is possible to reuse green sand by the way of adjusting the composition to get the lost additives and moisture replenished. The entire pattern itself is eligible to be reused for producing novel sand molds. The method of reuse can be continued for an indefinite period. In 1950, casting process got automated partially. They have been in great demand for developing production lines since then.
Spin Casting: Sand Casting is better known as Centrifugal Rubber Mold Casting (CRMC). It implies utilization of centrifugal force for producing castings out of rubber mold. As a customary practice, a mold having shape of a disc gets spun through its ‘central axis’ at a pre-decided speed. The material used for casting is usually thermoset plastic in the liquid form or a molten metal. It gets poured into the mold through the opening at its centre. Corresponding to the solidification of metal, or the setting of thermoset plastic, the spinning of the filled mold takes place.
Normally, organic rubber or vulcanized silicone is used as a mold-making substrate in spin casting. Vulcanization takes place in the middle of process of mold-making. After the successful completion of vulcanization process, venting and gating must be undergone by the mold. This implies carving of channels for ensuring proper material flow and air during the course of casting. Your best bet for preforming the proccessed is to either use a scalpel or knife. The mold complexity is directly proportional to the time required in implementation of venting and gating.
Metal Casting ZOne is a new community website all about Home and DIY Metal Casting. Come by today and join the site for free and you get a free Metal Casting Basics EBook just for signing up! Come by MetalCastingZone.Com Today for your free Ebook on Metal Casting.
No comments:
Post a Comment